Product Details:
|
Model: | HZ-7016 | Load: | 2265g,three Groups |
---|---|---|---|
Runner Diameter: | 150 Mm | Rotor Speed: | 45±5 Times/minute |
Counter: | LCD 0-999999 Times, Shows 6 Figures | Sandpaper Model: | 40# 、60#(Optional) |
Size: | 710mm×440mm×560mm(L×W×D) | Weight: | About 115kg |
Rated Voltage: | AC~220V 50HZ | Guarantee: | 1 Year/12months |
Highlight: | 50HZ Rubber Testing Machine,Multipurpose Rubber Testing Machine,Stable NBS Rubber Abrasion Tester |
Product description:
The DIN roller abrasion resistance tester for rubber products is applicable to the abrasion test of elastic materials, rubber, tire, conveyor belt, transmission belt, sole, soft synthetic leather, leather, etc. It has the characteristics of energy, good reproducibility and easy operation. The DIN abrasion tester is made according to the test standard DIN-53516 and is applicable to the abrasion resistance measurement of rubber products. It is a very suitable testing machine for comparison test and product balance inspection and classification.
Standards:
Rubber product DIN roller abrasion resistance tester conforms to DIN-53516, ISO/DIS-4649, GB-9867
Test methods:
Specimen on a test machine, plus some of the load, friction rotation of sandpaper specimen, check its wear resistance.
Standard:
ASTM D1360-94,DIN-53516, ISO/DIS-4649, GB-9867
Specification:
Model |
HZ-7016 NBS Rubber Abrasion Tester |
Load |
2265g, three groups |
Runner diameter |
150 mm |
rotor speed |
45±5 times/minute |
Counter |
LCD 0-999999 times, shows 6 figures |
Sandpaper model |
40# ,60#(Optional) |
Size |
710mm×440mm×560mm(L×W×D) |
Weight |
about 115kg |
Rated voltage |
AC~220V 50HZ |
Test principle:
Under the specified contact pressure and on the given area, the sample shall be at a certain angle with the sandpaper, and the abrasion resistance of the sample caused by friction on a certain grade of sandpaper shall be measured.
The sandpaper package is pasted on the surface of the drum, and the sample is pressed tightly on the drum with sandpaper to make the sample move laterally along the drum.
Abrasion is produced at one end of the cylindrical sample. Measure the mass loss value of the sample and calculate the volume abrasion based on the density of the sample